Polymaker PolyMide™ PA612-CF (carbon fiber reinforced nylon)

PolyMide™ PA612-CF is a carbon fiber reinforced polyamide filament based on a copolymer of PA6 and PA12. Thanks to its chemical structure, this product has lower moisture sensitivity compared to PA6/66 and PA6-based materials, and better mechanical properties than PA12-based materials. In addition, the carbon fiber reinforcement and Warp-free technology enhance the dimensional stability of the prints produced with this material.

Color: Black
Diameter: 1.75mm
Weight: 500g

Note: Use of a wear resistant nozzle is recommended

Print Settings
Nozzle: 250˚C – 300˚C
Bed: 25˚C – 50˚C
Fan Speed: Off
Print Speed: 30mm/s – 60mm/s
Print Surface: Glass, PEI, BuildTak with a coat of Magigoo Pro PA 
Direct Drive: Retraction Distance: 3mm
Indirect Drive: Retraction Distance: 6mm

Annealing settings: 80˚C for 6h

Drying settings: 100˚C for 8 hours (only if the material has absorbed moisture)

Mechanical Properties
Young’s Modulus: 7453 ± 656 (MPa)
Tensile Strength: 105.0 ± 5.0 (MPa)
Bending Strength: 169.0 ± 4.7 (MPa)
Charpy Impact Strength: 13.34 ± 0.52 (kJ/m2)

Thermal Properties
Heat Deflection Temperature (ISO 75 1.8 MPa): 196 ˚C
Heat Deflection Temperature (ISO 75 0.45 MPa): 215 ˚C
Melting Temperature: 220 (°C)

PolyMide™ PA612-CF Technical Data Sheet